Ventana óptima de un hierro dúctil austemperizado con aleantes carburizadores

Cesar Yeshua Becerra-Mayorga; Marissa Vargas-Ramírez; Alejandro Cruz-Ramírez; Jesús García-Serrano; Eduardo Colin-García

doi:10.29057/icbi.v10iEspecial7.9823

Cesar Yeshua Becerra-Mayorga Universidad Autónoma del Estado de Hidalgo https://orcid.org/0000-0002-5213-2764
Marissa Vargas-Ramírez Universidad Autónoma del Estado de Hidalgo https://orcid.org/0000-0002-5968-6196
Alejandro Cruz-Ramírez Instituto Politécnico Nacional https://orcid.org/0000-0002-0972-596X
Jesús García-Serrano Universidad Autónoma del Estado de Hidalgo https://orcid.org/0000-0003-3016-1684
Eduardo Colin-García Instituto Politécnico Nacional https://orcid.org/0000-0002-9922-9555

DOI: https://doi.org/10.29057/icbi.v10iEspecial7.9823

Palabras clave: Hierro dúctil austemperizado, Austenita retenida con alto contenido de carbono, austemperizado, ferrita, ausferrita

Resumen

En este trabajo se llevaron a cabo tratamientos térmicos de austemperizado a un hierro dúctil con 0.45 % Cr y 0.2 %V para determinar la ventana óptima de proceso. El hierro dúctil se austenitizó a 900 °C durante 60 min; posteriormente se austemperizó a 285 °C por diferentes tiempos entre 15 a 90 minutos. Durante el tratamiento térmico se obtienen dos fases conocidas como ferrita acicular y austenita con alto contenido de carbono. Esta última fase se cuantifica con rayos X. El valor más elevado de austenita (35%) se obtuvo en la muestra tratada a 60 minutos; mientras que el menor (21.7%) se obtuvo a los 15 minutos. Adicionalmente, se evaluó la dureza de las muestras. El mayor valor de dureza (59.9 HRC) se obtuvo en la muestra tratada a 30 minutos; mientras que la dureza más baja (53.9 HRC) se obtuvo a los 90 minutos. Evaluando los datos la ventana del proceso se encuentra entre 60 y 90 minutos.

Descargas

La descarga de datos todavía no está disponible.

Citas

Abioye, A. A., Atanda, P. O., Abioye, O. P., Afolalu, S. A., & Dirisu, J. O. (2017). Microstructural characterization and some mechanical behavior of low manganese austempered ferritic ductile iron. International Journal of Applied Engineering Research, 12, 14435–14441.

Ahmadabadi, M. N., Ghasemi, H. M., & Osia, M. (1999). Effects of successive austempering on the tribological behavior of ductile cast iron. Wear, 293–300. DOI: https://doi.org/10.1016/S0043-1648(99)00163-5.

Alagarsamy, A. (2014). Cast irons. American Foundrymen’s Society, 489–581.

ASM Handbook Committee. (1990). ASM Handbook Volume 1: Properties and Selection: Irons, Steels and High-Performance Alloys. ASM International. Alabama, Estados Unidos.

Cemal, M., Bayram, A., & Isik, B. (2005). The effects of austempering temperature and time onto the machinability of austempered ductile iron. Materials Science and Engineering, 147–153. DOI: 10.1016/j.msea.2005.07.005.

Colin, E., Cruz, A., Reyes, G., Téllez, J., & Magaña, A. (2021). Microstructural and mechanical assessment of camshafts produced by ductile cast iron low alloyed with vanadium. Metals, 11(1), 146. DOI: https://doi.org/10.3390/met1101014.

Dawson, J. V., & Sage, A. M. (1989). High strength cast irons containing vanadium: Annealed ductile irons and high carbon gray irons. The Foundryman, 479–489.

Gazda, A. (2010). Analysis of decomposition processes of ausferrite in copper-nickel austempered ductile iron. J. Therm. Anal. Calorim, 102, 923–930. DOI: https://doi.org/10.1007/s10973-010-0804-y.

Hayrynen, K. L. (2002). The production of austempered ductile iron (ADI). In World Conference on ADI, 57–65. DOI: https://doi.org/10.1016/j.msea.2014.12.038.

Hernández-Rivera, J. L., Campos Cambranis, R. E., & De la Garza, A. (2011). Study of microstructural evolution and mechanical properties exhibited by non-alloyed ductile iron during conventional and stepped austempering heat treatment. Materials & Design, 4756–4762. DOI: https://doi.org/10.1016/j.matdes.2011.06.030.

Laino, S., Sikora, J. A., & Dommarco, R. C. (2008). Development of wear-resistant carbidic austempered ductile iron. Wear, 265, 1–7. DOI: http://dx.doi.org/10.1016/j.wear.2007.08.013.

Miller, R. L. (1964). A rapid method for the determination of retained austenite. Trans. ASM, 57, 892–899. DOI: http://dx.doi.org/10.1007/s11041-019-00417-y.

Nasir, T., Northwood, D. O., Han, J., Zou, Q., Barber, G., Sun, X., & Seaton, P. (2011). Heat treatment-microstructure-mechanical/tribological property relationships in austempered ductile iron. WIT Transactions of Engineering Science, 71, 159–170. DOI: http://dx.doi.org/10.2495/SECM110141.

Pereloma, E. V., & Anderson, C. S. (2006). Microstructure and properties of austempered ductile iron subjected to single and two-step processing. Mater. Sci. Technol, 22, 1112–1118. DOI: http://dx.doi.org/10.1179/174328406X114216.

Prasad, R. P., & Putatunda, S. K. (2003). Investigations on the fracture toughness of austempered ductile irons austenitized at different temperatures. Mat. Sci. Eng. A, 349, 136–149. DOI: http://dx.doi.org/10.1016/S0921-5093(02)00633-0.

Rao, P. P., & Putatunda, S. K. (1997a). Influence of microstructure on fracture toughness of austempered ductile iron. Metallurgical and Materials Transaction, 1457–1470. DOI: https://doi.org/10.1007/s11661-997-0208-1.

Rao, P. P., & Putatunda, S. K. (2003b). Investigations on the fracture toughness of austempered ductile iron alloyed with chromium. Materials Science and Engineering, 254–265. DOI: http://dx.doi.org/10.1016/S0921-5093(02)00633-0.

Rezvani, M., Harding, R. A., & Campbell, J. (1997). The effect of vanadium in as-cast ductile iron. Journal of Cast Metals, 1–15. DOI: https://doi.org/10.1134/S0031918X19050016.

Sheikh, M. (2019). Influence of austempering heat treatment on ductile iron. PakJET, 2, 38–40. DOI: https://doi.org/10.51846/vol2iss2pp38-40.

Swain, S. K., Panda, R. K., Mishra, J. P., & Sen, S. (2012). Phase investigation of austempered ductile iron. Orissa J. Phys, 19, 73–80.

Yescas, M. A., & Bhadeshia, H. K. D. H. (2002). Model for the maximum fraction of retained austenite in austempered ductile iron. Mat. Sci. Eng. A, 333, 60–66. DOI: https://doi.org/10.1016/S0921-5093(01)01840-8.