Modification of the behavior of the mortar with respect to humidity by adding zeolite
Abstract
In this article, the characteristics of a mortar generated by substituting fifty percent of its volume of sand for a similar one of zeolite were compared with respect to a control mixture to which no zeolite was added. This in order to establish whether the presence of said material modified the behavior of the mortar with respect to its internal humidity, as well as to establish whether the reversible absorption capacity of the zeolite was still active despite being integrated into a cementing paste. To achieve this, samples of both mixtures were subjected to the initial maximum moisture absorption test and the total absorption test at 24 hours, also determining their internal humidity throughout the day to establish whether there were differences in both materials, before environmental humidity. Finally, the results obtained did show clear differences in all the tests carried out in favor of the mixture with zeolite, so it was concluded that the hypothesis was correct.
Downloads
References
Águila Higuero, V. (2010). Características físicas y mecánicas de hormigones reforzados con fibras de: vidrio, carbono y aramida. Trabajo Fin de Máster, Universidad Politécnica de Madrid, Departamento de Ingeniería Civil: Construcción, Madrid.
Andrada, R., Baronetto, C., Positieri, M., Oshiro, A., Raggiotti, B., & Sánchez Soloaga, I. (2012). Evaluación térmica de morteros elaborados con zeolita como porcentaje de sustitución de aglomerante. ASADES, 16(08), 223-230.
Bosch, P., & Schifter. (1997). La zeolita, una piedra que hierve. Ciudad de México.
CIMEC. (2018). ¿Qué es el coeficiente de correlación de Pearson? Obtenido de https://www.cimec.es/coeficiente-correlacion-pearson/
Comino, P., & Romero, J. (julio/septiembre de 1996). El GRC Compuesto de matriz cementicia reforzado con Fibra de vidrio AR. Materiales de construcción, 79-89.
Edificación, O. N. (2017).
Determinación de la granulometría de la arena de sílice utilizada en la preparación de los morteros de cementantes hidráulicos, NMX-C-329-ONNCCE-2016.
Flores Lozano, E., López de Juambelz, I., Velázquez Vázquez , D., Moreno Pérez , E., & Hernández Ávila, J. (12 de Diciembre de 2020). Comparativa del Impacto de la diatomita, perlita y zeolita en el comportamiento térmico y estructural del mortero. Pädi, 8(Especial), 5-13.
Gobierno, S. d. (2012). Evaluación de la conductividad o resistencia térmica de los materiales aislantes NOM-018-ENER-2011.
IMCYC. (Julio de 2011). El concreto en la obra. Problemas, causas y soluciones. Ciudad de México: Instituto Mexicano del Cemento y del Concreto. Obtenido de Propiedades del concreto: http://www.imcyc.com/cyt/julio04/CONCEPTOS.pdf
Lorrio Domene, L. (2011). Análisis del comportamiento térmico de las zeolitas como material ligero, alternativo a la arcilla expandida, en hormigones para formación de pendientes. Trabajo fin de Máster para Arquitecta Técnica. (E. d. técnica, Ed.) Madrid, España: Universidad Politécnica de Madrid.
Quintero Ortiz, L. A., Cruz Hernández, R. A., & Peña Santos, D. Y. (octubre-diciembre de 2014). Efecto del contenido de agua sobre la resistencia y la velocidad de pulso ultrasónico del concreto. (U. D. Caldas, Ed.) Tecnura, 18(42), 103-113.
Raggiotti, B. B., Positieri, M. J., Locati , F., Murra, J., & Marfil, S. (2015). Zeolita, estudio de aptitud como una puzolana natural aplicada a hormigón estructural. Revista de la construcción, 14(2), 14-20.
.
Rivero Nogueiras, V. (2016). Análisis Medio Ambiental de los aislamientos térmicos en la construcción. Coruña: Universidad de Coruña.
SCT. (2017). CMT. Características de los Materiales. En S. d. Transporte, CMT. Características de los Materiales . Ciudad de México: Secretaría de Comunicaciones y Transportes.
Vera Barrios, B. S., & Ledezma Elizondo, M. T. (2018). Pasta cementicia mejorada con adición de Zeolita y Hierro en polvo para morteros de pega o junteo. ingeniería, investigación y tecnología, 19(2), 223-238.